HIGH SPEED STEEL

  

Shape : Grade :

AISI T1 Steel

Standards

AISI T1

T1
DIN 3355
C Si Mn P S Cr W V
0.65 - 0.80 0.20 - 0.40 0.10 - 0.40 0.03 0.03 3.75 - 4.00 17.25 - 18.75 0.90 - 1.30

 

Virat Special SteelsAISI T1

Grade Brief:

Virat Special Steels is the biggest provider & Stockiest of AISI T1 Steel.
AISI T1 is a tungsten kind tool steel. Very high resistance to put on and to softening. Just right longevity , reducing potential & deep hardening response. This grade is on the whole used for turning, planning & slotting instruments, tapes, twist drill, threading dies, profile slicing instruments, broaching instruments & reamers.

 

HSS T1 / DIN 3355 / AISI T1 is a high speed tool steel with an 18% tungsten content that has strong toughness, wear resistance , High purity with least inclusions and glasses , good mechanical properties coming from fine and uniform grain size and good cutting qualities. Tungsten-based tool steel with carbide structure without having Moly, resulting in difficult steel to cut qualities with high tensile strength. With 18% tungsten, it is the best effective high-speed steel grade based on W, with excellent wear resistance, red hardness, and toughness. Tungsten in this tool steel makes it simple to cut parameters with high tensile strength - hardness up to 63-66 HRC following heat treatment.


Mode of Supply

Virat Special Steels is the largest stockiest and supplier of AISI T1 Steel in flat, square and round bar. We provide steel in all sizes as your requirements. AISI T1 die steel is available in flat, square and round shape. Consult our team who will assist you for AISI T1 steel query.

 

aisi-t1-steel

Steel Properties

Standard hiqh-speed steel qrade. Itswell-balanced alloycomposition forms the basis of its high_touqhness and good clll:ting edge retention, render'lng it suitable for a large variety of applications.

 

Mechanical Properties:

 

Tensile Strength 1220-1380 MPa
Hardness 63-65 HRC
Modulus of elasticity 190-210 GPa

Physical Properties

The average oxygen concentration, carbon content, and chromium content of T1 / DIN 3355 / AISI T1 are 0.10%, 0.85%, and 5%, respectively. This remarkable combination produces components with great hardness—able to achieve Rockwell C66 or higher—and superior red hardness, allowing them to be used even during prolonged cutting operations.

 

Thermal Conductivity at °C 20 350 700
W/(m*K) 32.8 23.5 25.5

 

Heat Treatment & Processes:

Heat treatment

HSS T1 / DIN 3355 / AISI T1 is a popular option among metalworkers because of its durability and heat resistance, thus having the right heat treatment is critical to ensuring these properties. Specialists will advise heating the metal to a specified temperature before cooling it, followed by an annealing procedure to harden it further. To maximize the benefits of tool steel T1, the cooling pattern should be carefully regulated by qualified personnel. According to the procedure throughout the heat treatment process, this specialized material may gain strength and stress resistance for even more dependable industrial performance.

 

Forging:

T1 / DIN 3355 / AISI T1 high speed steel should be slowly and consistently warmed to 850–880 °C.For T1 / DIN 3355 / AISI T1 tool steel, raise the forging temperature to 1050–1130°C.After forging, T1 / DIN 3355 / AISI T1 hss tool steel has to cool extremely slowly.

 

Annealing:

The temperature range for annealing is 1600–1650 °F. Cool to 1000° F gradually at a rate of 35° F per hour. Media that are insulating are used for optimum outcomes. 2 hours at the desired temperature.

 

Stress Relieving:

Temperature ranges 1100-1300° F .Stress relieve after rough machining.

 

Preheating:

Preheat time in a furnace is 1/4 hour per inch of thickness at a temperature of 1500–1550°F. Heating up to temperature as slow as possible.

 

Hardening:

Harden at 2375° F for best wear resistance. Harden at 2275° F for optimum toughness and hardness.

 

Tempering:

Temper T1 / DIN 3355 / AISI T1 high-speed steel shortly after it has been quenched. Allow at least two hours. It is advised to temper twice. 2 hours is the typical tempering time. The recommended temperature for cutting tools is 1000-1075° F and 1100-1200° F for shock tools.

 

Soft annealing °C Cooling Hardness HB
870-900 slowly max. 270

 

Stress-relief annealing °C Cooling
630 - 650 Furnace

 

1st pre-heating °C 2nd and 3rd Hardening °C Quenching Tempering °C Hardness after Teperature HRC
up to approx. 400 in an air-circulating furnace 850 and 1050 1190 - 1230 Saltbath, at least 550 °C Oil ,Air at least twice 530-560 64 – 66

DIN 2344
H13

Application

For all metal-cutting tools for roughing or finishing such as twist drills, diverse milling cutters, thread dies, broaches, reamers, countersinks, thread chasers, circular saw segments, shaping tools and woodworking tools. Also highly suitable for cold-forming tools such as cold extrusion rams and dies, as well as cutting and precision cutting tools, plastic moulds with elevated wear resistance and screws.


Metal Weight Calculator:
Shape:
Quantity:
Diameter
Length:
Results
Calulated Weight: 0 Kgs / 0 Lbs

Addition to other Grades:

HCHCR-D2 Steel , HCHCR-D3 Steel , P20+Ni Steel , P20 Steel , DB6 Steel , H13 Steel, H11 Steel, H21 Steel, H10 Steel, H12 Steel, M2 Steel, M35 Steel, M42 Steel, T1 Steel, DIN 2379 Steel, DIN 2080 Steel, DIN 2738 Steel, DIN 2311 Steel, DIN 2714 Steel, DIN 2344 Steel , DIN 2343 Steel, DIN 2581 Steel, DIN 2365 Steel, DIN 2606 Steel, DIN 3343 Steel, DIN 3243 Steel, DIN 3247 Steel, DIN 3355 Steel AISI D2 Steel, AISI D3 Steel, AISI P20+Ni Steel, AISI P20 Steel, AISI L6 Steel, AISI H13 Steel, AISI H11 Steel, AISI H21 Steel, AISI H10 Steel, AISI H12 Steel, AISI M2 Steel , AISI M35 Steel, AISI M42 Steel , AISI T1 Steel

Products

 

  • C-545, Sector-37, Pace City - II, Gurgaon 122001 (Haryana) India
  • C-146, Focal Point, Phase - V, Ludhiana 141010 (Punjab) India

 

payment